Method for forming an optical wave guide coupler

ABSTRACT

A method of forming an optical radiation waveguide integral with a glass substrate in combination with a coupler for coupling optical radiation into the waveguide. The waveguide and coupler are formed by thermal diffusion of ions in glass and the coupler may be shaped by inserting the glass into the solution a certain distance to form the waveguide with additional insertion of the substrate into the solution for shaping the coupler.

United States Patent 1 1 1111 3,888,648 West et al. June 10, 1975 METHOD FOR FORMING AN OPTICAL 3,806,328 4/1974 Yoshida et al 65/DIG. 7

WAVE GUIDE COUPLER OTHER PUBLICATIONS [75] Inventors: Edward J. West, Silesia, Md.;

Thomas G Giauorenzi, Alexandria Supplement to The Journal of The Japan Soc1ety of Va Physics, Vol. 39, pp. 63-70, 1970. Optical Waveguides Formed by Thermal Migration of Asslgneel The Ulllted States of Amellca a5 Ions in Glass, Giallorenzi et al., received by printer represented by the Secretary of the O b 1972, 1240-1245. Navy, Washington, DC.

22 i Man 1974 Primary Examiner-Robert L. Lindsay, Jr.

Attorney, Agent, or FirmR. S. Sciascia; Arthur L. [21] Appl. No.: 448,581

Branning; Melvin L. Crane Related U.S. Application Data [62] Division of Serv No. 313,003, Dec. 7, 1972, Pat. No. [57] ABS 3,802,761- A method of forming an optical radiation waveguide 52 U.S. c1. 65/30- 65/4- 65/DIG. 7 integral with a g a ubstrate in combination with a 51 1m. 01 C03C 25/02- (3030 15/00 coPpler couplmg optlcal radlation Into the ve- 53 Field f Search 65/30 DIG 7 gulde. The waveguide and coupler are formed by ther- IIIIIIIIIIIIIIIIIII mal diffusion of ions in glass and the coupler may be [56] References Cited shaped by inserting the glass into the solution a certain distance to form the waveguide with additional inser- UNITED STATES PATENTS tion of the substrate into the solution for shaping the 3,647,406 3 1972 Fisher 65/30 coupler.

3,697,384 7/1972 Colson et al.

3,765,855 10/1973 Larrick 65/30 10 Claims, 11 Drawing Figures A "r I 1, I I 17 117' HEATER PATENTEDJUHIO m5 .SHEET FIG. 2.

H EATER FIG. 1.

FIG. 5.

HEATER FIG. 3.

METHOD FOR FORMING AN OPTICAL WAVE GUIDE COUPLER STATEMENT OF GOVERNMENT INTEREST This application is a Division of application Ser. No. 313,003 filed Dec. 7, 1972 now U.S. Pat. No. 3,802,761.

BACKGROUND OF THE INVENTION This invention relates to optical waveguides and optical radiation couplers for optical waveguides and more particularly to the method of combining an optical coupler and rectangular optical waveguide integral with a substrate.

Herefore rectangular optical waveguides have been fabricated by securing a glass with a higher index of refraction onto a substrate with 'a lower index of refraction in air. Other waveguides have been formed by sputtering, ion exchange, ion bombardment, vacuum evaporation, liquid phase epitaxy and plasma polymerization. Sputtered films have been made of different materials which resulted in films with propagation losses of less than ldb/cm. Polymerized organosilicon films have resulted in low loss films as low as 0.05 db/cm. Ion bombarded films produced in fused silica have resulted in films with 0.2 db/cm losses. Ion exchange has been previously used in the manufacture of low loss optical fibers as well as in the fabrication of planar and three-dimensional waveguides in glass. Sputter type waveguide and couplers have been set forth in a published article: Experiments on Light Wave in a Thin Tapered Film and a New light-wave Coupler by P. K. Tien and R. J. Martin; Applied Physics Letters, volume 18, number 9, pages 398-401, May 1, 1971.

SUMMARY OF THE INVENTION This invention is directed to a method of forming thin film radiation waveguides and couplers for a rectangular optical waveguide and to a method of forming thin film optical radiation waveguides and couplers. The optical waveguides and couplers are formed by ion exchange. A thin piece of glass may be inserted into a molten solution containing ions such as AgNO KNO and TlNO wherein the Ag K or Tl ions are exchanged for lighter ions such as Na and Li in the glass. Therefore, the surface layer in which the ions are exchanged have a higher index of refraction than the glass portion with unexchanged ions to form a waveguide on the surface of the glass substrate. With the glass immersed only partially of its length into the molten solution, a coupler is formed at the area corresponding to the transition region from exchange to unchanged glass. By slowly immersing the glass into the solution after having formed the waveguide, the slope of the coupler may be changed to provide different angular shaped couplers. By two step diffusion, i.e., exchange of Ag K", or T1, for Na and Li followed by an exchange of Na and Li for Ag K*, or Tl a buried waveguide may be formed within the substrate. A buried waveguide may also be joined by diffusion limiting processes when the waveguide is forced by ion exchange. Throughout the specification, the waveguide is considered to be rectangular.

STATEMENT OF THE OBJECTS It is therefore an object of the present invention to easily and reproducibly produce optical waveguide edge couplers.

Another object is to provide a method by which uniform optical waveguide edge couplers may be produced.

Still another object is to form an optical waveguide coupler by an ion exchange method.

Yet another object is to form a combined optical coupler and optical waveguide integral with a substrate.

While still another object is to form an optical waveguide within a substrate as a part of the substrate.

Other objects and advantages to the invention will become obvious from a review of the following specification when considered with the drawing.

BRIEF DESCRIPTION OF THE DRAWING FIG. 1 illustrates a system for forming a waveguide onto a substrate.

FIG. 2 illustrates the region of ion exchange or waveguide region along the surface of the substrate.

FIG. 3 illustrates a substrate immersed percent of its length into a molten ion solution to form an optical waveguide optical waveguide coupler.

FIG. 4 illustrates the ion exchange region depicting the integral optical waveguide optical waveguide coupler.

FIG. 5 illustrates a waveguide buried beneath a surface layer of the substrate.

FIGS. 6a and 6b illustrate the ion exchange profiles created in stirred AgNO baths.

FIGS. 7a, b, and c illustrate the ion exchange profiles created in unstirred AgNO baths.

FIG. 8 illustrates the ion exchange stirred KNO bath.

DESCRIPTION OF THE INVENTION It is well known that optical radiation waveguides may be created by placing a medium upon a substrate wherein the medium placed upon the substrate has a higher index of refraction than that of the substrate. Also, the index of refraction of the waveguide medium has an index of refraction higher than that of the medium in which the waveguide is placed such as air.

The refractive index of glass is related to both the density of the glass and to the electronic polarizability of the constituent ions within the glass. It has been determined that the index of refraction of glass may be changed by diffusing ions such as Ag K, or Tl into the glass replacing lighter ions of Na and Li which were diffused out of the glass.

Optical radiation waveguides and couplers have been made by use of substrates of similar composition such as a soda-lime silicate glass with minor proportions of MgO and A1 0 all giving similar results. Other substrates slightly larger than microscope slides having the following composition Al-4 percent, Na-l2 percent, Ca-7 percent, Mg-2 percent and Si the major constituent have also been used. Aluminosilicate glasses have been found to be superior to soda-lime glass with the best results produced by ion exchange in molten Ag- N0 Good results of fabricating waveguides and couplers have been obtained by using a substrate glass having the molar composition 12 percent Li O, 12 percent Na O, 12 percent A1 0 64 percent SiO profile for a In earring out the process for fabricating surface layer waveguides on a substrate, the substrate 11 is immersed into a molten solution 12 containing ions to be exchanged in the glass substrate, for example, AgNO KNO or TlNO as shown in FIG. 1. By way of example, the substrate is immersed entirely into a molten solution of AgNO having a temperature range of from about 225C to about 270C for a period of 24 hours. During the ion exchange, the molten solution is stirred resulting in a surface layer ion exchange depth 13 of from m to 20m. During the process, the Ag* ions diffuse into the surface layer of the substrate as represented in'FIG. 2 and the Na and Li ions diffuse into the solution.

In order to fabricate a composite optical waveguide with a tapered optical radiation coupler on a substrate, the same process is followed except that the substrate is immersed only partially for example (75 percent) into the molten solution containing ions. This is shown by example in FIG. 3. During a partial immersion of the length of the substrate into the molten solution, a transition region of several hundred optical wavelengths long which varies in silver content from that of the waveguide silver concentration to zero concentration is formed. This transition region is tapered in silver concentration thereby forming a tapered waveguide coupler 14 in conjunction with the waveguide as shown by solid line in FIG. 4.

It has been determined that a longer tapered edge may be formed by slowly lowering the substrate into the molten concentration once the waveguide has been formed. During lowering of the substrate, the Ag ions diffuse further into the surface and along the tapered waveguide and to form a longer tapered end 15 as shown by dotted lines in FIG. 4. Thus, the slope and length of the optical coupler may be controlled and produced with a desired slope.

In the above discussion surface waveguides and/or waveguide couples have been discussed. It has been determined that the process may be expanded to form optical waveguides below the surface as shown in FIG. 5. Such waveguides may be made by two different methods. A substrate 11 is placed into a molten solution 12 of ions just as explained previously to form surface waveguides and/or waveguide-waveguide couplers. In one method, the substrate with the previously formed integral surface waveguide is immersed into a bath or solution of NaNO;, in order to deplete the surface layer 16 of silver. The surface silver ions exchange with the sodium ions in the bath. The exchange is from the outer surface inwardly. Thus, the surface silver ions are depleted while the sodium ions diffuse into the surface layer of the substrate. Therefore, a layer of silyer ions remain within the body of the substrate sandwiched between the main substrate body and the surface layer 16 on the outside of the silver layer within the body. It has been determined that the surface area of a previously formed silver waveguide may be depleted sufficiently to form an internal waveguide by immersing the substrate-waveguide into a NaNO bath at a temperature of 225C for a period of 4 hours.

A second method of forming a buried silver waveguide within the body of a substrate is to immerse the substrate into an unstirred molten solution of AgNO maintained at a temperature of 225C for a period of 24 hours. During this time, the sodium ions migrate out of the substrate while the silver ions migrate into the substrate replacing the sodium ions. Due to the fact that the molten solution is not stirred, the outer layer of silver ions are depleted and replaced by sodium ions thereby leaving a layer of silver ions buried within the body of the substrate about 6 microns from the outer surface.

Since buried waveguides are removed from the glass air interface, and because of its graded index profile, such waveguides have low propagation losses since surface scattering will be reduced.

As explained above a waveguide coupler may be formed by immersing the substrate about percent of its length into a molten solution of ions where a tapered boundary exist between the waveguide in the dipped portion and the unchanged substrate above the dipped portion. The above method for forming buried waveguides may be followed to produce waveguidewaveguide couplers that are buried below the surface of the substrate.

It has been determined that thermal ion exchange index change of AgNO is much greater than that of KNO Each of these are much greater than TlNO The following table lists the measured indices of refraction for the propagating waveguide modes formed by dipping the substrate in a stirred bath of the molten ion change solution for 24 hours.

The glass substrate used in the above index of refraction examples for AgNO was STARLUX a plate glass having the following chemical composition Al-4 percent, Na-l2 percent, Ca-8 percent, Mg-2 percent and Si the major constituent, manufactured by A. S. G. Industries, Kingsport, Tennessee. The glass used for K was a special Anchor Hocking glass having the following composition: 12 percent Li O, 12 percent Na O, 12 percent A1 0 64 percent SiO Thallium exchange for 24 hours dipping periods at 250C did not produce good reproducible waveguides and have not been shown.

FIGS. 6(a) and 6(b) illustrate the ion exchange profiles created in stirred AgNO baths. In FIG. 6(a) the calcium and sodium profiles in an untreated STAR- LUX.substrate are shown. FIG. 6(b) illustrates the silver, sodium and calcium profiles in 24 hours dipped substrates with the AgNO bath maintained at 225C.

FIGS. 7a, b, and 0 illustrate the ion exchange profile created in unstirred AgNO baths. FIG. 7a presents the Al and Mg profiles in an untreated STRALUX substrate. FIGS. 7b and 7c, the peak of the silver profiles are shown displaced in toward the substrate interior as discussed previously for forming waveguides buried within the interior of a substrate. Temperature and time same as above for FIGS. 6a and b.

F IG. 8 illustrates the ion exchange profile for a stirred KNO bath with a temperature of 365C for a period of 24 hours.

The optical waveguides made in accordance with the principles of this invention are reproducible and are of low loss. Losses of 0.1 db/cm have been measured. Silver exchanged waveguides have been found to degrade in performance with time with degradation accompanied by a discoloring of the waveguide surface. However, treatment with HNO has been found to restore such waveguides to their original performance. Good waveguides with loss less than 0.5 db/cm do not de grade nor could degradation be promoted by exposure to intense untraviolet radiation.

Obviously many modifications and variations of the present invention are possible in the light of the above teachings. It is therefore to be understood that within the scope of the appended claims the invention may be practiced otherwise than as specifically described.

What is claimed and desired to be secured by Letters Patent of the United States is:

1. A method of forming an optical waveguidecoupler in a rectangular glass substrate along the outer surfaces by exchange of component ions, which comprises:

heating to a molten solution a compound comprising ions to be exchanged with ions in said substrate;

extending said glass substrate linearly into said molten solution with a linear portion thereof extending from said molten solution;

leaving said glass substrate extended into said molten solution at the same depth for a time period sufficient to exchange a layer of component ions along the surfaces of said glass substrate extending within said molten solution with ions of said molten solution surrounding said substrate; and

removing said substrate from said solution at the end of said time period;

whereby a waveguide layer is formed along the surface with a tapered edge extending above said molten solution at the transition region between the ion exchange layer formed within the molten compound and the unexchanged region of said substrate;

said tapered edge of ion exchanged area extending downwardly and inwardly from the outer surface to the inner face of the ion exchange region.

2. A method as claimed in claim 1 wherein:

said compound is selected from a group consisting of AgNO KNO and TlNO 3. A method as claimed in claim 2, wherein;

said compound is AgNO;,.

4. A method as claimed in claim 2, wherein;

said compound is KNO 5. A method as claimed in claim 3, wherein;

said compound is heated to a temperature of from 225 270C for a period of about 24 hours.

6. A method as claimed in claim 4, wherein;

said compound is heated to a temperature of about 365C for a period of about 24 hours.

7. A method forming an optical waveguide as claimed in claim 1 which includes;

constantly stirring said molten solution during said ion exchange period.

8. A method of forming an optical waveguide in a glass substrate by exchange of component ions as claimed in claim 1, wherein;

the solution is unstirred, resulting in a depletion of ions at the glass bath interface whereby a buried layer of ions remain and a waveguide below the surface is formed.

9. A method of forming an optical waveguide in a glass substrate as claimed in claim 1, wherein;

subsequent to forming an ion exchange layer in said substrate said substrate is lowered slowly into the solution an addition amount thereby changingthe slope of the tapered edge of the transition region between the ion exchange region and the unexchanged region.

10. A method of forming an optical waveguide in a glass substrate by exchange of component ions as claimed in claim 1, wherein;

subsequent to removing said substrate from said molten solution, said substrate is immersed into a NaNO bath for a time period to deplete the surface layer.

whereby a layer of exchanged ions remain below the surface of said substrate. 

1. A METHOD OF FORMING AN OPTICAL WAVEGUIDE-COUPLER IN A RECTANGULAR GLASS SUBSTRATE ALONG THE OUTER SURFACES BY EXCHANGE OF COMPONENT IONS, WHICH COMPRISES: HEATING TO A MOLTEN SOLUTION A COMPOUND COMPRISING IONS TO BE EXCHANGED WITH IONS IN SAID SUBSTRATE; EXTENDING SAID GLASS SUBSTRATE LINEARLY INTO SAID MOLTEN SOLUTION WITH A LINEAR PORTION THEREOF EXTENDING FROM SAID MOLTEN SOLUTION; LEAVING SAID GLASS SUBSTRATE EXTENDED INTO SAID MOLTEN SOLUTION AT THE SAME DEPTH FOR A TIME PERIOD SUFFICIENT TO EXCHANGE A LAYER OF COMPONENT IONS ALONG THE SURFACES OF SAID GLASS SUBSTRATE EXTENDING WITHIN SAID MOLTEN SOLUTION WITH IONS OF SAID MOLTEN SOLUTION SURROUDING SAID SUBSTRATE; AND REMOVING SAID SUBSTRATE FROM SAID SOLUTION AT THE END OF SAID TIME PERIOD; WHEREBY A WAVEGUIDE LAYER IS FORMED ALONG THE SURFACE WITH A TAPERED EDGE EXTENDING ABOVE SAID MOLTEN SOLUTION JAT THE TRANSITION REGION BETWEEN THE ION EXCHANGE LAYER FORMED WITHIN THE MOLTEN COMPOUND AND THE UNEXCHANGED REGION OF SAID SUBSTRATE; SAID TAPERED EDGE OF ION EXCHANGED AREA EXTENDING DOWNWARDLY AND INWARDLY FROM THE OUTER SURFACE TO THE INNER FACE OF THE ION EXCHANGE REGION.
 2. A method as claimed in claim 1 wherein: said compound is selected from a group consisting of AgNO3, KNO3, and TlNO3.
 3. A method as claimed in claim 2, wherein; said compound is AgNO3.
 4. A method as claimed in claim 2, wherein; said compound is KNO3.
 5. A method as claimed in claim 3, wherein; said compound is heated to a temperature of from 225 - 270*C for a period of about 24 hours.
 6. A method as claimed in claim 4, wherein; said compound is heated to a temperature of about 365*C for a period of about 24 hours.
 7. A method forming an optical waveguide as claimed in claim 1 which includes; constantly stirring said molten solution during said ion exchange period.
 8. A method of forming an optical waveguide in a glass substrate by exchange of component ions as claimed in claim 1, wherein; the solution is unstirred, resulting in a depletion of ions at the glass - bath interface whereby a buried layer of ions remain and a waveguide below the surface is formed.
 9. A method of forming an optical waveguide in a glass substrate as claimed in claim 1, wherein; subsequent to forming an ion exchange layer in said substrate said substrate is lowered slowly into the solution an addition amount thereby changing the slope of the tapered edge of the transition region between the ion exchange region and the unexchanged region.
 10. A method of forming an optical waveguide in a glass substrate by exchange of component ions as claimed in claim 1, wherein; subsequent to removing said substrate from said molten solution, said substrate is immersed into a NaNO3 bath for a time period to deplete the surface layer. whereby a layer of exchanged ions remain below the surface of said substrate. 